A developer of new plastics technologies is applying low-temperature die drawing to take advantage of a new raw material: expanded, oriented, wood-filled polypropylene (EOW-PP). It looks and feels almost indistinguishable from natural wood but is 150% stronger. It’s also 300% stronger than ordinary PP and close enough to the strength of steel that the term “plastic steel” is no great exaggeration.
“We haven’t been able to break it yet. It just bends,” says Frank Maine, president of SHW (Synthetic Hardwood) Technologies Inc. in Guelph, Ont., the developer of EOW-PP.
This unusual new material is made by a combination of two metalworking processes: solid-state extrusion and die drawing. Solid-state deformation processes like ram extrusion are typically used to shape high-value, non-melting plastics like UHMW polyethylene and PTFE into tubes and sheets, not to form inexpensive commodity resins. Orienting of PP film and fiber is commonplace, but orienting a solid PP profile has been limited to lab work in a few universities.
In the early 1990s, researchers at the Aluminum Company of Canada Ltd. (Alcan) in Kingston, Ont., spent six years ram extruding unmelted PP into highly oriented rods of enormous strength. The process requires two steps. First, PP is extruded conventionally into billets—solid, round, or rectangular profiles that are cut to 15-20 in. lengths. The billets are then heated to slightly below the melting point and are ram extruded with a very high draw ratio into thin profiles. Haul-off tension around 450 psi keeps the profiles from relaxing before they cool.

Bending Machine

Alcan patented the process and material but halted the project after the price of aluminum plunged. Symplastics Ltd. in Orangeville, Ont., a plastics processor already experienced in deformation processing of UHMW-PE sheet, bought Alcan’s patents and lab line and spent three more years of R&D on the process.
After three years, Symplastics’ only commercial success with the OPP profiles were small rods made for Frank Maine, who machined them into unbreakable drumsticks for musicians. “Drummers objected to the look of the plastic,” Maine recalls. “They liked the performance of the PP drumsticks, but wanted the sticks to look like wood.”
So Symplastics added 8% wood flour to the billets, which made the rods look and feel remarkably like wood. Wood-filled rods acquired less orientation but still had impressive strength. Eventually Symplastics found the R&D too costly and sold the patents and lab line to Maine, who set up SHW to try to commercialize more applications for the super-strong material.
One such application is unfilled OPP beams for automotive side-impact bars, which were tested recently side by side with steel beams. The load at failure for OPP was 30% below that of steel. But while the steel beam snapped when it failed, the OPP beam only delaminated. These preliminary test data were released earlier this month at the Society of Automotive Engineers show in Detroit by Dr. Phillip Bates, Assoc. Prof. at the Royal Military College in Kingston, Ont.
Die drawing also went much faster—up to 30 ft/min, vs. 4 ft/min for ram extrusion alone. At such a speed, it may be possible to run billet extrusion in line with die drawing, Maine speculates. And with die drawing, Maine doesn’t need to use the ram, thereby saving energy. Pushing the billets takes 3000 psi, but die drawing takes only 1800 lb of tension to do the same work. The ram now only pushes the first 5 in. of the billet through the die, enough for the puller to grab.
Die drawing may allow larger profiles to be oriented. Ram extrusion of unfilled PP is limited to small rods, probably not over 1 in. diam., because orientation takes place only in the resin close to the compression-chamber walls. The larger the profile, the greater the ratio of weaker, unoriented core to stronger, oriented skin. Maine speculates that die drawing of wood-filled PP may cause the orientation to be more evenly distributed across the profile.
Maine says die drawing can also speed the solid-state extrusion of unfilled PP. He has not yet tested the resulting product to ascertain the level of property improvement in unfilled material.